STAUF SGH 50
3Pages

STAUF SGH 50 Fast hardening 2 component silicate reaction resin Technical Datasheet Product number ✓ 116600 Special features Application range ✓ low odour ✓ easy to use ✓ fast setting ✓ Embedding or surface mounting of metal elements in concrete, terrazzo, stone, marble etc. ✓ rim-pull sealing of cement floor cracks ✓ Repair of steps made from concrete, stone or artificial stone. ✓ Sealing of cracked or hollow composite or heated screeds sanded mastic asphalt screed concrete floors concrete walls calcium sulphate (flow) floors magnesite and plaster floors masonry stone, ceramic, terrazzo, tiles cement floors Product properties ✓ good adhesion to various materials ✓ high strength ✓ solvent-free ✓ quick curing Suitable cleaner ✓ STAUF Solvent cleaner ✓ STAUF Cleaning agent Required quantities per m2 ✓ Depending on quantity and size of local separations ✓ For a crack width of 5 mm and a crack depth of 5 cm (screed is cut in half) approx. 3 to 4

Drying time ^ approx. 60 minutes at 20 °C Room climate at work site ^ Minimum 18 °C, maximum 75% rel. humidity, preferably max. 65% Transport requirements ^ not below + 5 °C ^ not below + 10 °C ^ cool Shelf-life ^ 9 months Available packaging ^ resin: 320 g ^ hardener: 480 g Allocation article-no. hardener 2c ^ 116610 Mixing ratio component A ^ 1 Mixing ratio component B ^ 1,5 EXAMINATION OF SUBFLOOR Prior to processing, the subfloor must be checked according to the standard DIN 18356, DIN 18365 or corresponding national standards. The subfloor shall be examined according to the standards...

PROCESSING Widen the crack in the floor to approx. 5 mm using an angle sander, also cut the floor across the crack and install floor brackets. Pour the casting resin into the crack immediately after mixing and wipe off with smooth blade. After that the resin has to be sprinkled with quartz sand. ACCESSIBILITY Further processing at +20°C approx. after 1 hour, fully accessible after 24 hours. LIMITATION OF LIABILITY The foregoing representations are based on the results of our most current product and material testing and are of a non-obligatory advisory nature only since we have no control...