EGM-100 Epoxy resin grout TECHNICAL DATA High-strength, high-adhesion epoxy resin grouting material with good fluidity DISCRIPTION EGM-100 epoxy resin grout includes three components, i.e. A (resin), B (hardener) and C (filler). The product uses high-quality resin and refined filler, with 100% solid content. It does not contain volatile substances and other harmful solvents to the human body, etc. It can be used after the three components contained in each group of epoxy resin grout are completely mixed at room temperature without additional ingredients. CONSTRUCTION TECHNOLOGY PRODUCT HIGHLIGHT The water-based epoxy resin grouting material additive is consisted of three components. First, add component A into a clean standby barrel, then add component B in proportion and mix it fully, add it to the characteristic mortar after mixing, and then use it; bonding, etc. that are much better than that of cement-based materials, and it has higher early strength. 2. Low exothermic peak: it can provide up to 120 minutes (25°C) operation time, and it is suitable for Use weighing tools to strictly weigh water-based epoxy resin, water-based epoxy curing High strength and early strength: it can provide mechanical performance such as compression, agent, characteristic mortar and other components according to the proportioning of products; large-volume grouting. Mixing ratio: 3. No shrinkage: ensure that the grouting layer is in full contact with the bearing surface after the final A: B: C = 1:1:14, Scooping water-based epoxy resin and water-based epoxy curing agent shall use their own forming, ensure the high accuracy of equipment installation. spoons. Remember not to cross use, otherwise raw materials will be scrapped; under the harsh physical conditions of -50°C to +80°C alternating freezing and thawing, vibration and Fully stir the mixed waterborne epoxy resin and waterborne epoxy curing agent for 2 ~ 5 Excellent creep resistance: epoxy resin grout can be used for a long time without plastic deformation minutes with low-speed mixer until the mixture turns white and uniform, and there is no obvious trace during compression, ensuring long-term accuracy of equipment positioning. stirring. Tools and containers shall be cleaned without stickiness, and then special mortar shall be added while mixing; equipment that may cause the cement-based grouting layer to burst. Mixing quantity: Strictly control every quantity of waterborne epoxy grouting material according to the construction site environment (mainly temperature) and construction speed (mainly the number of Excellent toughness: epoxy resin grout can dissolve any dynamic load transmitted by moving 6. Corrosion resistance: it can withstand long-term contact corrosion with acids, alkalis, salts, greases and other chemicals. participants and the difficulty of operation), especially in outdoor construction operations. The waterborne epoxy raw materials should be stored in a cool and dry place, and the mixing operation should be completed in cool place, otherwise the gel will be wasted if this product is mixed too much. Construction: Brush the old interface once with aqueous epoxydiluent (aqueous epoxy resin: aqueous epoxy curing agent = 1:1). Then construct the aqueous epoxy resin slurry; Cleaning: Remove the dust and slag on the old construction interface in advance and keep it dry. Please clean the tools with water after construction. 1. Secondary grouting installation of high-vibration equipment such as compressors, pumps, presses, grinders, ball mills, etc. 2. Grouting for the equipment foundation area that is susceptible to chemical attack. 3. Grouting in areas that suffering strong pressure such as track foundations, bridge support seats. 4. Strengthening of anchor bolts, steel bar planting and building structure concrete, etc. 5. Using as self-leveling mortar in surfaces such as concrete, stone, steel, and wood boards are used as. 6. The rigid connection of iron, iron tie rods and tie rods. Sino-sina Building Materials Co.,Ltd. | www.wcrete.com | [email protected] | +86 15373872353

TECHNICAL DATA CONSTRUCTION PROCESS ■ Mixing: 1) Use a portable mixer (200-250rpm) to fully mix A (resin) and B (hardener) for about 3 minutes;2) Add C (fller) into the low-speed and high-power mixer (15-20rpm) to mix it with the mixture of A and B. Stir fully until theaggregate joint is infiltrated, and it will take about 5-10 minutes.3) n order to ensure the fuidity of the mixture when the temperature is low, the amount of C (fller) can be appropriatelireduced (max1/2 material can be reduced). ■ Grouting: 1) The grouting should be grouted from one side to the other; it can be squeezed but not...