Sikagard®-62
3Pages

PRODUCT DATA SHEET Sikagard®-62 2-part epoxy protective coating PRODUCT DESCRIPTION ENVIRONMENTAL INFORMATION Sikagard®-62 is a two part, rigid, 100 % solids, coloured high build epoxy resin based protective coating. Conformity with LEED v2009 IEQc 4.2: Low-Emitting Materials - Paints and Coatings APPROVALS / STANDARDS Sikagard®-62 may only be used by experienced professionals. ▪ Coating for concrete protection according the requirements of EN 1504-2:2004, Declaration of Performance 0206060100100000011008, certified by FPC Notified Body and provided with CE marking ▪ DWI, Reference No. DWI.56.4.197, Approved under Regulation 31(4)(A) of teh Water Supply (water Quality) Regulatios 2016 SI No.614 ▪ Chemical resistant protective layer on concrete, stone, cementitious mortars and renderings, epoxy cement, epoxy resin based products and steel ▪ Lining in storage tanks and silos ▪ Anti-corrosion coating on steel in food processing plants, sewage works, farms, agricultural enterprises, chemical and pharmaceutical facilities and beverage industry Solvent free Good mechanical and chemical resistance High build Impervious to liquids Easy to mix and to apply PRODUCT INFORMATION Chemical Base Epoxy resin Appearance / Colour Light Grey, Light Green Shelf Life Part A: 12 months Part B: 12 months From date of production if stored properly. Storage Conditions The packaging must be stored properly in original, unopend and undamaged sealed packaging, in dry conditions at temperatures between +5 °C Product Data Sheet Sikagard®-62 July 2020, Version 04.04 020606010010000001

and +30 °C. Protected from direct sunlight. Density Mixed resin approx. ~1.37 kg/l Density values determined at +23°C Solid Content TECHNICAL INFORMATION Shore D Hardness Mechanical resistance Taber Abraser Taber Abraser Taber Abraser Tensile adhesion strength Chemical Resistance Please contact Sika technical service for specific information. Thermal Resistance Exposure Permanent max. 7 days max. 12 hours APPLICATION INFORMATION Mixing Ratio Part A : Part B = 3 : 1 by weight Layer Thickness Substrate Temperature +8 °C min. / +40 °C max. Minimum 3 °C above dew point, beware of condensation...

exposed. All dust, loose and friable material must be completely removed from all surfaces before application of the product, preferably by brush and/or vacuum. Open voids and blowholes need to be closed with a suitable Sika® pore filling mortar. The roughness of the substrate needs to be levelled with a suitable Sika® rendering and levelling mortar. Steel Surface Steel surface must be prepared mechanically using abrasive blast cleaning. The level SSPC-SP 10 “near white metal blast cleaned” or level Sa 2 ½ according to ISO EN 12944-4 has to be achieved. Welds and joints have to be prepared...