PRODUCT DATA SHEET SikaForce®-335 GG SELF-LEVELLING 2-COMPONENT PU-GROUT FOR EMBEDDING OF GLASS PANELS TYPICAL PRODUCT DATA (FURTHER VALUES SEE SAFETY DATA SHEET) Properties Chemical base Colour (CQP001-1) mixed Cure mechanism Density (uncured) mixed (calculated) Solid content Mixing ratio Viscosity (CQP538-2) Application temperature Pot-life (CQP536-3) Shore D hardness (CQP023-1 / ISO 7619-1) Tensile strength (CQP036-2 / ISO527-2) Elongation at break (CQP036-2 / ISO 527-2) Glass transition temperature (ISO 11359-2) Shelf life CQP = Corporate Quality Procedure C) test speed 5 mm/min by volume by weight Brookfield - RVT 6/20 Brookfield - RVT 2/50 (mixed) Brookfield - RVT 6/20 10 000 mPa·s A ambient 15 ─ 30 °C 30 minutes A 60 B 7.7 MPa B, C 20 % B, C 5 °C D 12 months E A) 23 °C / 50 % r.h. D) cured 4 months at 23 °C / 50 % r.h.; heating rate 5 K/min DESCRIPTION PRODUCT BENEFITS SikaForce®-335 GG is a pourable, self-level- ▪ Stress-free glass embedding process ling, two-component polymer grout based on ▪ Allows homogenous load distribution polyurethane resin. It has been designed for ▪ Long pot-life, easy to use embedding of monolithic or laminated glass ▪ Room temperature curing panes in U-shaped support channels for ▪ Solvent-free standard glass railing, frameless or postless guard rail and balcony glazing. It is suitable for indoor and outdoor applications, if sealed with Sikasil® WS product. PRODUCT DATA SHEET SikaForce®-335 GG Version 02.01 (03 - 2020), en_GB 012104533350001000 SikaForce®-010 Hardener Isocyanate derivatives brown B) curing 28 days at 23 °C / 50 % r.h. E) storage between 10 °C and 30 °C AREAS OF APPLICATION SikaForce®-335 GG is designed for embedding of monolithic or laminated glass panes in Ushaped support channels for standard glass railing, frameless or postless guard rail and balcony glazing. It is suitable for indoor and outdoor applications, if sealed with Sikasil® WS product. This product is suitable for experienced professional users only. Test with actual substrates and conditions have to be performed to ens
Open the catalog to page 1CURE MECHANISM The curing of SikaForce®-335 GG takes place by a chemical reaction of the two components. Higher temperatures speed up and lower temperatures slow down the curing process. CHEMICAL RESISTANCE In case of chemical or thermal exposure, conduct project related testing. METHOD OF APPLICATION Consult the General Guideline “Glass Embedding” for construction details and dimensions prior to the product application. Surface Preparation Surfaces must be clean and dry. Application The procedure for manual application is as follows: Stir the base part thoroughly until it is mixed...
Open the catalog to page 2All Sika France SAS catalogs and technical brochures
-
SikaMembran® Universal
2 Pages
-
Sikafloor® PurCem® HB-23
4 Pages
-
Sika Comfortfloor® PS-65
4 Pages
-
Sika Comfortfloor® PS-27
4 Pages
-
Sika Comfortfloor® PS-23
4 Pages
-
SikaCor® EG-5
4 Pages
-
Sikagard®-62
3 Pages
-
Sikasil® FS-665 SL
2 Pages
-
Sikasil®-670 Fire
3 Pages
-
Sikasil® WS-605 S
2 Pages
-
ADHESIVES AND WEATHER SEALING
28 Pages
-
Sika® PowerCure
2 Pages
-
references_sarnafil
8 Pages
-
sikalastics
2 Pages
-
sarnafil
12 Pages