Technical Specifications:
- Surface Treatment: S2 PVDF on both sides.
- Yarn: PES HT 1100 Dtex.
- Weight: 1050 g/sqm (31 oz/sqyd) as per EN ISO 2286-2.
- Width: 267 cm (105.1 in) with a tolerance of +1mm/-1mm.
- Tensile Strength: 420/400 daN/5cm (warp/weft) according to EN ISO 1421 and ASTM D 751-00 Cut Strip.
- Tear Resistance: 55/50 daN (warp/weft) as per DIN 53.363 and ASTM D 751-00 Trapezoid.
- Adhesion: 12 daN/5cm as per EN ISO 2411.
- Flame Retardancy: Euroclass B-s2,d0/EN 13501-1, with various ratings including M2/NFP 92-507 and B1/DIN 4102-1.

Management Systems:
- Quality: ISO 9001 compliant.
- Environmental Communication: ISO 14021 compliant.

Environmental Impact:
- LEED Heat Island Effect: Solar Reflectance Index (SRI) >95%.
- Life Cycle Assessment (LCA): Global warming potential and energy/water consumption metrics provided for different end-of-life scenarios.

Dimensional Stability:
- Elongation: Less than 1% for both warp and weft after 24 hours under 10daN/5cm load.
- Residual Elongation: Less than 0.4% as per EN 15977.

Solar Optical Values:
- Solar Transmittance: 6%.
- Solar Reflectance: 78% to 81%.
- Solar Factor: 9.5% to 12%.
- Visible Light Transmittance: 4%.
- Visible Light Reflectance: 90%.
- UV Transmission: 0%.

Thermal and Acoustic Performance:
- Thermal Conductivity: Approximately U=5.6/6.4 W/sqm/°C.
- Acoustic Weakening Index: Approximately 14dBA as per ISO 717-1.

Additional Information:
- Total Thickness: 0.78 mm.
- Coating Thickness: 200 microns at the top of the yarns.
- Varnish Adhesion Longevity: QUV A 4000 h pass Scotch tape test.

Warranty and Responsibility:
- Warranty details are case-specific and do not apply to mobile structures.
- Buyers are responsible for product application, transformation, and compliance with local standards and safety rules.

Contact Information:
- Headquarters: +33 (0)4 74 97 41 33
- Local Representative: Available on the Serge Ferrari website.

Recycling and Sustainability:
- Serge Ferrari offers an operational recycling chain and promotes the use of secondary raw materials to combat natural resource depletion.