EPODUX IM 209
4Pages

Maestria [V PEIHTURES & 5TSTEMES EPODUX IM 209 "Tolerant " High Build Epoxy High build epoxy coating tolerant to humidity. Protection of metal structures in open air or immersed in freshwater, seawater or brackish water : - Locks, - Jetties, - Sheet piles, - Stakes, - Pipes, - Water treatment plants (please contact our technical department),... - Good adherence on cold or damp surfaces (non dripping) : this feature enables to coat active forced ducts without any losses associated with maintenance interruptions. - Applicable in thick layers (600 microns, no sagging). - Good anti corrosion protection. - May be immersed 30 min after coating (polymerisation under water). - Over 1500 colour tints possible with our "Industry" tinting machine system. Notes : - The film properties, excluding the colour, are not affected by actinic radiation. - A change of tint (whitening) may occur during immersed polymerisation; the other characteristics of the coating remain unchanged. : Brand ACQPA 35511 Is used in the following certified systems : Im2 ANI 950, Im2 ANI 1232, Im2 ZNI 1284 and C5GNV 866 : Is used in the following systems registered in the FNP under numbers 1036, 1050, 1054,1065, 1066, 1067 and 1095. : Is used in the waterproofing paint system referenced IMP-3. TECHNICAL DATA Gloss level Colours Number of components Mix ratio, by weight Mix ratio, by volume Specific gravity Solids volume Solids weight Typical thickness (dry) Typical thickness (wet) Theoretical spreading rate : Satin : Beige, White, Light Grey, Black, according to RAL / AFNOR :2 : 83/17 : 74,5/25,5 : 1,55 +/- 0,05 g/cm3 : 85,00 +/- 3% : 90,15 +/- 2% : from 50 to 400 pm : from 60 to 470 pm : 16,7 m2/l for 50 pm dry and 2,1 m2/l for 400 pm dry For further information, visit our website : www.maestria.fr Contact : accueil@maestria.fr

EPODUX IM 209 "Tolerant " High Build Epoxy SURFACE PREPARATION New steel « heavy duty use » Abrasive blast cleaning at Sa 2 % according to ISO 8501-1 : 2007.Roughness profile : Mid G according to ISO 8503-2 (Ra 10-12,5 pm). High pressure water jet cleaning (UHP) at Wa 2 1/2 - according to ISO 8501-4 : 2006. Galvanized steel : Fine abrasive brushing or pickling with METONET followed by clear water rinsing. Metallization : The substrate will be in accordance with standard NF EN ISO 2063. In case of damage or defects observed on the surface please refer to the recommendations of the standard...

Version 03/22 Page 3/4 EPODUX IM 209 "Tolerant " High Build Epoxy Thickness achievable after several passes *The maximum dilution rate is reserved for application to metalized substrate when EPODUX IM 209 is used as tie coat. CLEANING SOLVENT : 67-232 v02 For further information, visit our website : www.maestria.fr Contact : accueil@maestria.fr

EPODUX IM 209 "Tolerant " High Build Epoxy CURING TIME Page 4/4 Laboratoire Recherche & Developpement - Usine - Administration Z.i -1, rue Denis Papin - 09100 PAMIERS - Tel. 05 61 67 97 40 - Fax : 05 61 67 05 47 Contact: accueil@maestria.fr - Site internet: www.maestria.fr This description sheet is designed to inform customers about the properties of our product. The information is based on our current knowledge. However, this information cannot replace an appropriate description of the nature and condition of the base to be painted. Techniques and technology are constantly developing and...