Inorganic Boards
2Pages

Catalog excerpts

Inorganic Boards Product Data Sheet Product Description I-2300 is an insulating material produced by blending high purity, synthetic alumina-silica fibers with high purity silica binders. The high temperature capability is enhanced by employing ammonia stabilized colloidal silica rather than a sodium stabilized product. I-2600 is an insulating material produced by blending aluminosilicate fibers, alumina fibers and silica fibers with high purity silica binders. The alumina fibers form a matrix within the material, and give it high temperature capability. I-2800 is an insulating material produced by blending aluminosilicate fibers, alumina fibers and silica fibers with high purity silica binders. The polycrystalline alumina fibers form a matrix within the material, and give it high temperature capability. The high temperature capability is further enhanced by employing ammonia stabilized colloidal silica rather than sodium stabilized product. I-A5 is an economical, ultra high temperature insulating material produced by blending alumina-silica fibers, alumina fibers and silica fibers with high purity silica binders. The alumina fibers form a matrix within the material, and give it high temperature capability. The high temperature capability is further enhanced by employing ammonia stabilized colloidal silica rather than sodium stabilized product. Enhance mechanical properties with one of our post treatments using ultra-high purity ammonia stabilized colloidal silica No organic binders Complex shape capability Low thermal conductivity and minimal heat storage High resistance to thermal shock and spalling Low shrinkage Light weight Publication Date: 2 October 2020 Code: SH.06 1 of 2 Bullnose tiles Burner blocks Combustion chamber construction Diffusion furnaces Flue and exhaust stack liners Furnace components General molten metal contact Peep door frames and plugs Heat shields High temperature gaskets and seals Hot tops for super alloy casting Molten aluminum contact Semiconductor processing equipment Shapes for laboratory furnaces Shapes in ammonia reformers www.morganthermalceramics.com Email: marketing.tc@morganplc.com Thermal Ceramics i

Open the catalog to page 1

Inorganic Boards Product Data Sheet Modulus of Rupture, MOR, MPa (psi), *unfired Compressive strength @ 5% deformation, MPa (psi) Compressive strength @ 10% deformation, MPa (psi) Permanent Linear Shrinkage, %, 24 hours Chemical Composition, % Thermal Conductivity, W/m•K (BTU•in/hr•ft2), ASTM C201 Whilst the values and application information in this datasheet are typical, they are given for guidance only. The values and the information given are subject to normal manufacturing variation and may be subject to change without notice. Morgan Advanced Materials – Thermal Ceramics makes no...

Open the catalog to page 2

Inorganic Boards 2Pages

Catalog excerpts

All Morgan Advanced Materials catalogs and technical brochures

Inorganic Boards
2Pages