Deutsches Institut fur Bautechnik Zulassungsstelle fur Bauprodukte und Bauarten Bautechnisches Prufamt Eine vom Bund und den Landern gemeinsam getragene Anstalt des offentlichen Rechts * E-Mail: [email protected] provisions of Member States European Technical Approval ETA-13/0549 Trade name English translation prepared by DIBt - Original version in German language Manufacturing plants WerksmaGig hergestellte Schuttung aus Schaumglasschotter Factory made cellular glass loose fill Diese Zulassung umfasst I 11 Seiten einschlieBlich 1 Anhang This Approval contains \ 11 pages including 1 annex Europaische Organisation fur Technische Zulassungen European Organisation for Technical Approvals

European technical approval ETA-13/0549 English translation prepared by DIBt LEGAL BASES AND GENERAL CONDITIONS This European technical approval is issued by Deutsches Institut für Bautechnik in accordance with: - Council Directive 89/106/EEC of 21 December 1988 on the approximation of laws, regulations and administrative provisions of Member States relating to construction products1, modified by Council Directive 93/68/EEC2 and Regulation (EC) N° 1882/2003 of the European Parliament and of the Council3; Gesetz über das In-Verkehr-Bringen von und den freien Warenverkehr mit Bauprodukten zur Umsetzung...

European technical approval ETA-13/0549 English translation prepared by DIBt SPECIFIC CONDITIONS OF THE EUROPEAN TECHNICAL APPROVAL Definition of the products and intended use Definition of the construction product This European technical approval applies to the thermal insulation fill made of recycled waste glass powder. This foam glass gravel consists of factory made particles of cellular foamed glass, with typical size 10/50 mm or 10/75 (nominal sizes d/D). Typical loose bulk density, dry, is in the range of approximately 125 – 190 kg/m³. The thermal insulation fill "MISAPOR" is manufactured...

European technical approval ETA-13/0549 English translation prepared by DIBt Release of dangerous substances The thermal insulation is manufactured from recycled glass. Table 1 shows the limit values of selected chemical substances determined in the approval testing after digestion for subsequent determination of aqua regia soluble according to EN 136577. Table 1: Limit values of chemical substances row 1 2 3 4 5 6 7 8 Chemical substance arsenic (As) plumb (Pb) cadmium (Cd) chromium (Cr) copper (Cu) nickel (Ni) quicksilver (Hg) zinc (Zn) analytical method Note: In addition to the specific clauses...

European technical approval ETA-13/0549 English translation prepared by DIBt Particle size distribution The particle size distribution is measured in accordance with EN 933-111, applying sieve sizes according to EN 933-212. Nominal aggregate size in mm is for "MISAPOR 10/50" d/D = 10-50 mm and for "MISAPOR 10/75" d/D = 10-75 mm. The cleanliness of the aggregate is G85/15 which means that the content of oversize material shall not exceed 15 % by mass and the undersize material shall not exceed 15 % by mass. Thermal conductivity The thermal conductivity is measured in accordance with EN 1266713...

European technical approval ETA-13/0549 English translation prepared by DIBt Table 5:Water absorption by total immersion on compacted specimens in percent by volume Product 28 days of total immersion % (by volume) Resistance to freezing and thawing The resistance to freezing and thawing is tested as follows: The compacted specimens are first exposed for long term water absorption by total immersion following EN 1208715 over a period of 28 days and then they are subjected to 25 freeze-thaw cycles. Each freeze-thaw cycle consist of a 9 hour frost exposure at minus 20 °C followed by 15 hours of...

European technical approval ETA-13/0549 English translation prepared by DIBt Load bearing capacity The oedometer modulus (compression stiffness) is measured in accordance with the giant oedometer test procedure described in the EOTA testing procedure ("Factory made cellular glass loose fill" Edition June 2005, Revision May 2013)17. The test procedure is similar to a standard drained oedometer test as described in EN 1997-218, but modified to suit a material with large particle size and low crushing resistance. The test was performed on test specimens with the actual degree of compaction (1.3...

European technical approval ETA-13/0549 English translation prepared by DIBt Settlement and creep strains The long-term creep behavior is measured in accordance with the giant oedometer test procedure described in the EOTA testing procedure ("Factory made cellular glass loose fill" Edition June 2005, Revision May 2013)17. The long-term creep behavior and the maximum settlement for the stress level are given in Table 10. Table 10: Long-term creep behavior Product Density after compaction (1.3 : 1) Stress level initial thickness reduction creep Expected total deformation after deformation test...

European technical approval ETA-13/0549 English translation prepared by DIBt The factory production control shall be in accordance with the control plan which is part of the technical documentation of this European technical approval. The control plan is laid down in the context of the factory production control system operated by the manufacturer and deposited with Deutsches Institut für Bautechnik22. The results of factory production control shall be recorded and evaluated in accordance with the provisions of the control plan. Other tasks for the manufacturer The manufacturer shall, on the...

European technical approval ETA-13/0549 English translation prepared by DIBt Assumptions under which the fitness of the thermal insulation fill for the intended use was favourably assessed Manufacturing The European technical approval is issued for the product on the basis of agreed data/information, deposited with Deutsches Institut für Bautechnik, which identifies the product that has been assessed and judged. Changes to the product or production process, which could result in this deposited data/information being incorrect, should be notified to Deutsches Institut für Bautechnik before the...