Starlike® Crystal Technical Specifications Science-based translucent epoxy gel (4Gen), enhanced with ultra-pure glass microbeads; waterproof, stain-resistant and UV-resistant, for the photochromic grouting of joints from 0 to 3 mm with high hygiene standards, for all types of mosaics, tiles, porcelain stoneware and large slabs. Product description Translucent epoxy gel (4th generation) for grouting joints from 0 to 3 mm in all types of mosaics, tiles, porcelain stoneware and large-format slabs. Patented formula enhanced with exclusive Level 2 technology using ultrapure glass microbeads that ensure light diffusion. The most effective photochromic colour-blending effect is achieved with glass materials that allow and amplify the passage of light, such as mosaics and transparent glass sheets or artistic mosaics For waterproof, stain-resistant and UV-resistant grout with exceptional chemical and mechanical resistance and resistance to thermal shock. Designed for exceptional ease of application and, thanks to state-of-the-art features, the mixture is extremely creamy, light, and super easy to spread and clean up. Classified as RG – EN 13888 and R2 – EN 12004 Starlike® Crystal is a highly innovative Litokol invention protected by Patent No. 102018000005366 Part A A blend of epoxy resins of varying molecular weights, manufactured under our own licence Extremely high concentration of recycled glass microbeads ~500 million/kg Ultra-fine particle size – range 60–180 µm Technical Speci

Rheological stabilisers and smart flow enhancers Part B Latest-generation non-corrosive polymeric linker Starlike® Crystal embodies Litokol’s ongoing scientific progress. It is designed using innovative raw materials to improve the installation experience, enhance safety and reduce environmental impact. Engineered with Colour technology Level 2 Recycled Crystal Microsphere® technology Zherorisk® EpoxyGel technology Defender Anti-Microbial Technology Contains 500 million glass microbeads per kg Microsphere diameter from 60 to 180 µm Recycled microspheres High-performance translucent epoxy gel...

Complies with HACCP/Regulation (EC) No 852/2004 on food hygiene Contains recycled glass microspheres (>75%) EPD Environmental Product Declaration LCA results for Global Warming Potential - Greenhouse Gases (GWP-GHG) Impact category Unit A1-A3 C1 C2 C3 C4 D Climate change GWP-GHG kg CO0 eq 1,85 4.38 1.21 x 0 6.73 x -2.76 Materials Ceramic and glass mosaics Porcelain stoneware Large formats Laminated stoneware slabs Ceramic tiles Glass sheets Self-levelling compounds Existing tiles Radiant heating systems Waterproofing products Decoupling membranes Metal Wood Aerated concrete Fibre-cement sheets...

Uses Floors - walls Interior - exterior Radiant heating systems Swimming pools - fountains SPA - Hammam Indoor wet areas - bathrooms and showers Exclusive locations Residential, public, commercial and street furniture Approved for marine use in accordance with the MED Directive 2014/90/EU Responsible Packaging Shelf life Customs heading Part A: Translucent gel Part B: Polymeric liquid Translucent Second-life recycled plastic buckets (Monopack A + 36 months in original packaging in a dry place. Do Compliance Washable with water Initial setting time Working set time ANSI A118.3 The material must...

Mixing ratio Mixing ratio Consistency of the mix Specific gravity of the mixture Pot life Joint width Application Permissible application temperatures Drying time for grouting Ready for foot traffic Commissioning Operating temperature Cleaning of equipment Applicable thicknesses Open time Recording time Drying time for grouting Application Part A: 94 parts by weight Part B: 6 parts by weight Epoxy gel 1.65 kg/dm3 ~ 90 min From 0 to 3 mm Starlike® Pro trowel From +10°C to +30°C 24 h 24 h 5 days - Swimming pools 7 days From -20°C to +100°C With water when the product is fresh. Mechanically once...

levelling compounds HydroLevel® 1-30 and X-Level® 0-10. To fully appreciate the superior flow and thixotropy of the innovative Epoxy Gel compound, mix the product using the specified mixing ratio. Cut a corner of the sachet containing the polymer catalyst (Part B) and pour it into the container holding Part A. It is recommended to pour out the entire contents of the catalyst, gradually rolling and squeezing the sachet from the sealed end towards the cut end. Polymerisation begins when the epoxy component is mixed with the hardener: this reaction creates new chemical bonds that form the threedimensional...

expansion, partition and perimeter joints. Starlike® Crystal is designed to be enhanced with the Starlike® Finishes range to achieve stunning aesthetic effects: blends of coloured glitter, metallic effects based on pearlescent mica, and ‘night vision' using photoluminescent technology will make grouted surfaces unique and exclusive. Add the pre-measured sachet of Starlike® Finishes, depending on the size, after mixing the catalyst (Part B), and mix thoroughly at low speed until a homogeneous mixture is obtained. Cleaning and Surface cleaning and the finishing of the grouting must be carried out...

Given the variations in quality across global ceramic production (e.g. polished porcelain stoneware) and the different mixtures used in the manufacture of mosaics available on international markets, it is recommended that a preliminary grouting test be carried out to identify any incompatibilities, cleaning difficulties or undesirable aesthetic effects. Do not add water, solvents or other foreign materials to the product Do not walk on the freshly grouted surface to prevent resin residues from damaging the flooring Remove any residues from the application process from the grouted surface promptly,...

The table below summarises the chemical resistance tests carried out in accordance with standard UNI EN 12808-1Chemical resistance of ceramic tiles grouted with Starlike® Crystal Intended use: wet areas and swimming pools Group Service Continuous Acetic acid Hydrochloric acid Citric acid Lactic acid Nitric acid Pure oleic acid Sulphuric acid Tartaric acid Ammonia in solution Caustic soda Sodium hypochlorite solution Active Cl concentration Caustic potash Calcium chloride Sodium chloride Sugar Unleaded petrol Diesel Extra virgin olive oil Lubricating oil Cleaning agent 1-4% Cleaning agent 2-5%...