Ottocoll M501 TRANSPARENT HYBRID ADHESIVE SEALANT. FOR INTERIORS AND EXTERIORS. ZHERORISK TECHNOLOGY OFFERS VERY LOW VOLATILE ORGANIC COMPOUND EMISSION RATE. Universal water-resistant adhesive. Transparent bonding. ADVANTAGES / FEATURES • Product exhibiths Very low volatile organic compound (VOC). Complies with the most stringent Global Air Quality Regulations. • Virtually invisible bonding • Rapid setting • Compensates for dynamic stress • Flexibility • Waterproof • Ready to use • No restrictions for transport over road, sea, air and rail • Compensates for movement • Bonding on wet surfaces and underwater • No hazard symbol on label 10.4 U.S. oz. (310 ml) cartridge (boxes with 20 pcs) For stress-compensating bonding and assembly of various materials, such as wood, wood-based materials, glass, metal (e.g. aluminum, stainless steel, anodized aluminum, brass, copper), plastics (e.g. rigid PVC, soft PVC, glass fiber reinforced plastic, etc.), mineral substrates (e.g. bricks, tiles, ceramics), fireproof panels (plasterboard, etc.) Production of cars and carriages, wagons and containers, metal and equipment, ship building Bonding of stone, natural stone and ceramic Stress-compensating bonding of mirrors on ceramic, glass, plastic, stainless steel, aluminum, wood, concrete, etc. Bonding of painted and enameled glass Bonding of stone, natural stone and ceramic The surfaces to be grouted or bonded must be perfectly clean, dry and free of dust, grease, oil and old paint. Cleaning non-porous surfaces: clean with OTTO Cleaner T (drying time about 1 minute) and a dry fiber-free cloth. Cleaning porous surfaces: clean the surfaces mechanically, e..g with a steel brush or a smoothing disc to remove loose particles. Remove the top part of the threaded part of the cartridge, screw in the plastic nozzle and cut it to the right angle depending on the desired diameter and profile. Insert the cartridge in a manual or air gun (with telescopic piston) and extrude the adhesive grout, being careful to avoid the entrainment of air. Once opened, the packages must be used in a relatively short time. The ideal operating temperature for the substrate and grout is between 59°F (15°C) and 77°F (25°C). The joints must be finished within the grout open time. Ottoseal M500 can be painted over. The compatibility of the varnish must be tested by performing a spot test. Prestare attenzione con l'uso di alcool o resina alchidiche poiché possono interferire con il processo di indurimento del sigillante e ridurre il tempo di asciugatura della vernice stessa.

The hardness and thickness of the varnish film may compromise the elasticity of the sealant and cause the varnish film to break. Do not allow polymerization in the presence of silicone sealants. Avoid contact with solvents during cross-linking. Since the product is hygro-hardening, allow sufficient exposure to air. Bonded elements may require extra support during the setting time. The extruded product must be compacted and made to penetrate deeply to encourage best adhesion and guarantee a watertight seal; it is advisable to use a metal or plastic trowel wet with soapy water. • Spread the product...

Powered by TCPDF (www.tcpdf.org) IDENTIFICATION DATA Polymerization Consistency of mix Specific gravity Film-forming time Setting in 24 hours Acceptable application temperatures Recommended application temperatures Serviceability Temperatures Set to light foot traffic Ready for use APPLICATION DATA Appearance Colors Customs code Shelf life Thick paste Crystalline 32141010 12 months in original packaging away from sources of heat and direct sunlight. Protect against frost. Set to thickness Shore hardness A Elastic modulus at 100% Elongation at break Tensile strength Data detection at temperature...