FastGel® S1+ Technical Specifications Elastic, crack-resistant, hydro-curing tri-polymer gel. Accelerated adhesion and rapid setting. Double pot life. Fluidotixo® - C5, with low cement content and reinforced with quartz microspheres, prevents the formation of cracks when laying tiles, porcelain stoneware, large slabs of all types and sizes, and natural stone. When combined with SafetyGel®, it forms the High-Adhesion Anti-Crack System – TileSafe® System. Product description Elastic, crack-resistant, tri-polymeric hydro-curing gel with double pot life, with accelerated adhesion and rapid setting, featuring the exclusive Fluidotixo® Anti-Fatigue compound, enhanced with quartz microspheres, formulated with low cement content (<25%), prevents the formation of cracks when laying tiles, porcelain stoneware of all types and sizes, and natural stone, both indoors and outdoors. Designed for high application reliability and thanks to state-of-the-art technology, the mixture is extremely creamy, fluid and thixotropic; it maintains its shape and thickness on both floors and walls with 100% wetting power, achieving double vertical slip resistance (T) and an extended open time of over 45 minutes. FastGel® S1+ develops accelerated, fracture-resistant elastic adhesion with ultra-high-performance rapid setting thanks to the synergy between the tripolymer system and the quartz microspheres. The dual curing mechanism ensures stable, tension-free installation and uniform adhesion of large-format tiles and stone slabs, whilst preventing the formation of stains on marble and natural stone susceptible to moisture. This advanced interaction enables FastGel® S1+ to deliver high performance with a rapid 12-hour curing time, even on challenging substrates or those subject to high stresses, such as overlays on old floors, underfloor heating systems, street furniture, balconies and terraces, where even extreme temperature fluctuations, moisture and mechanical stresses make adhesion conditions critical. Classified as C2FTE S1 – EN 12004 Technical Speci

TileSafe® System FastGel® S1+, when combined with SafetyGel®, forms the High-Adhesion Anti-Fracture System - TileSafe® System - engineered for the rapid installation of large-format tiles and slabs of any type and size in high-traffic areas, even on cracked substrates (up to 3 mm). The system helps to dissipate and neutralise substrate movements and tile expansion, whilst distributing heavy loads evenly without causing stress. Gel formula with a patent application filed FastGel® S1+ and the TileSafe® System are highly innovative Litokol inventions, with international patent applications filed...

This pseudoplastic behaviour allows for precise and highly fluid application, with superior adhesion to the substrate. The Fluidotixo® Antifatica compound has an extremely low apparent viscosity, which promotes exceptional fluidity under the trowel and 100% wettability. Designed for professional installers, the same mix delivers exceptional spreadability and reduces fatigue during prolonged installation of floor and wall coverings. Once applied, its ultra-thixotropic formula ensures that the shape and thickness remain unchanged on floors, with no sagging up to a thickness of 20 mm, even with...

The Fluidotixo® rheology allows for dynamic application: fluid under load, stable during application. The quartz microspheres reinforce the ITZ (Interfacial Transition Zone), transforming it into a monolithic elastic zone capable of absorbing movement, mechanical shocks and thermal variations without the propagation of cracks. Developed using the most advanced materials engineering, Fast Control® is an engineered hardening system based on the synergistic interaction between mineral hydration and hydro-curing cross-linking. This dual-curing mechanism triggers two complementary reactions: After...

System comprises two different technologies: 1. SafetyGel® - a 6-dimensional elastic anti-fracture membrane, capable of absorbing and compensating for movements in all six spatial directions before they are transmitted to the cladding. 2. FastGel® S1+ - a smart, elastic, crack-resistant tripolymeric gel with accelerated adhesion and rapid setting, enhanced with Crack Prevention® technology, capable of protecting the internal bond zone from microcracking and mechanical stress. Acts as a smart structural interface, protecting the adhesive transition zone (ITZ) and promoting a flexible, long-lasting...

Porcelain stoneware Ceramic tiles Large formats Laminated stoneware slabs Marble – Granite – Stone materials Natural stone Ceramic and glass mosaics Terracotta – Klinker Resin- or cement-based composites Insulating and sound-absorbing panels for interiors SafetyGel® Screeds Self-levelling compounds Levelling compounds Plaster Plasterboard Plaster and anhydrite Existing tiles Radiant heating systems Waterproofing products Decoupling membranes Aerated concrete Fibre-cement sheets Concrete Adhesive – levelling compound Floors – walls Interior – exterior Overlay Radiant heating systems Indoor wet...

In combination with SafetyGel® and SafetyTex Anti-Fracture for external use Cracked substrates New, uncured substrates or substrates of a different nature Change to a different laying pattern or tile size Installation near thresholds Installation over utility trenches Installation near expansion joints - partition joints Limitations Refer to national standards, such as UNI 11493 Ensure a full bed outdoors or under high loads Protect the tiled surface from heavy rain for at least 12 hours Temperature, ventilation, substrate absorption and installation material may affect the workability and setting...

Preparation of grey gel mixture Preparation of White Gel mixture Dough proving time Pot life Applicable thicknesses Open time Recording time Application Application temperatures Drying time for grouting Ready for foot traffic Commissioning Operating temperature Cleaning of equipment Class 5 - Fluidotixo Anti-Fatigue Water = 23-26% ~ 4.6-5.2 l / 20 kg Water = 24-27% ~ 4.8-5.4 l / 20 kg Notched trowel suitable for the tile size Wall: 3 hours - Floor: 3 hours With water when the product is fresh. Mechanically once the product has 6 mm trowel: ~ 2.5 kg/m2 8 mm trowel: ~ 3 kg/m2 10 mm trowel: ~ 3.5...