POLEPOX COAT 830-CC
9Pages

POLEPOX-PR 824 TRANSPARENT, EPOXY-BASED RESIN, USED AS AN ADHESIVE COMPONENT BETWEEN CONCRETE SURFACES AND EPOXY COATINGS GENERAL CHARACTERISTICS POLEPOX-PR 824 is a clear, epoxy, two-component resin, which is used as an adhesive component between concrete surfaces and final epoxy coatings.  Eliminates dust from decay in old & new floorings, reinforcing their durability. Offers high mechanical resistance and chemical protection against acid solutions, alkalis, oil, grease etc. It can be easily repaired locally if necessary, but must precede grinding of the surface with a sandpaper or mosaic machine. two-component epoxy resin liquid Application time: Final strength: Adhesive strength: Temperature for the application and drying of the material: SUBSTRATE REQUIREMENTS Basis: Appearance: TECHNICAL DATA Concrete quality: Moisture content:

PREPARATION APPLICATION Applied only on dry surfaces. Protected from arising humidity and free of materials that might prevent bonding e.g. dust, loose particles, grease etc. The success in the application depends on the right preparation of the underlay and use of the material.  Treatment of the surface with a mosaic machine, or with sandblast or rotor machine, depending on the thickness of the final coating. Good, dry cleaning of the surface from dust and residues with vacuum cleaner and use of squeegees. Caution must be taken so that temperature of the substrate as well as ambient air...

Working time of POLEPOX-PR 824 decreases when ambient temperature rises. Prolonged storage of partially used containers must be avoided as contact with atmospheric moisture will result in skinning and clouding of the product. It cannot be applied in thickness for filling cracks or holes. In this case it can only be used if mixed with fine dry sand. Do not mix or apply unless surface, air and material temperatures are over 12°C during the next 24 hours. Do not apply to floors if there is moisture in the subfloor drive or hydrostatic pressure. Prior precautions measurements of humidity with...

POLEPOX 833-CV GENERAL CHARACTERISTICS Epoxy two-component system. It offers strong bonding to the substrate and good conductivity that prevents the accumulation of static electricity on surfaces. It is used as an intermediate layer of the POLEPOX FLOOR 830-CC to assure uniform conductivity on the whole floor surface. TECHNICAL DATA two-component epoxy resin Application time: Final strength: Temperature for the application and drying of the material: Adhesive strength: SUBSTRATE REQUIREMENTS Moisture content: Concrete quality: Applied only on dry surfaces. Protected from arising humidity...

After hardening of the primer (2-12 hours depending on the ambient temperature) follows 2 the installation of the special copper-bands (conductors), in no less than 1,6m/m , in a grid formation and connection to the ground through a perimetrical cable. That means that in an 2 area of 100m there are needed 16 lines of copper-bands of 10m each. The 8 copper-bands are installed vertically and another 8 horizontally in a grid formation. Afterwards the surface is coated with POLEPOX 833-CV. Good mixing of components A (resin) & B (hardener) packed into separate containers in fixed weight...

POLEPOX 833-CV will yellow upon prolonged exposure to sunlight or high-intensity artificial lights. A urethane topcoat is highly recommended for color stability. The application must take place in well-aired places using protective gloves. Skin or eye contact must be avoided. Otherwise wash carefully with soap and water. For more information consult the material safety data sheet. The information given here is true, represents our best knowledge and is based not only on laboratory work, but also on field experience. However, because of numerous factors affecting results we offer this...

POLEPOX COAT 830-CC GENERAL CHARACTERISTICS Epoxy two-component colored system. It is used as a self-levelling coating on cement-based floors, in cases that static electricity causes problems. Offers permanent conductivity that prevents the appearance of static electricity charges on surfaces.  It has a conductivity resistance between 10 and 10 Ohm. It offers high mechanical resistance and chemical protection against acid solutions, alkalis, petroleum products, and a number of aggressive solvents. It is suitable for hospitals, computer rooms, laboratories, printing rooms, textile mills,...

Applied only on dry surfaces. Protected from arising humidity and free of materials that might prevent bonding e.g. dust, loose particles, grease etc. The success in the application depends on the right preparation of the underlay and use of the material.  Treatment of the surface with a mosaic machine. Good, dry cleaning of the surface from dust and residues with vacuum cleaner and use of squeegees. Caution must be taken so that temperature of the substrate as well as ambient air remains ο above 12 C during application and curing of the materials while relative environment humidity does...

Working time of POLEPOX COAT 830-CC decreases when ambient temperature rises. Prolonged storage of partially used containers must be avoided as contact with atmospheric moisture will result in skinning and clouding of the product. In Do not mix or apply unless surface, air and material temperatures are over 12°C during the next 24 hours. Do not apply to floors if there is moisture in the subfloor drive or hydrostatic pressure. Prior precautions measurements of humidity with special device are suggested. POLEPOX COAT 830-CC will yellow upon prolonged exposure to sunlight or high-intensity...