WHS: Profilé bois hybride Notice technique

WHS: Profile bois hybride Geolarri Architectural Eco-Technology Tolerances de section en mm: + 0.5 / - 2.0 dans certains cas, le pongage de la peau WPC pourrait creer des profils depassant ces dimensions nominales Classement au feu: Peut etre regie sur demande et en respectant diverses exigences et normes. Pour plus d'informations, consultez notre catalogue general en ligne page 36 Finition des surfaces: sablee, autres finitions disponibles sur demande. Pour plus d'informations, consultez notre site web www.geolam.com Fixation et installation de profils: consultez notre site web...

ANNEXES 0 - SOMMAIRE DES TESTS ET ESSAIS 1 - RÉSISTANCE À LA PROPAGATION DE L’HUMIDITÉ ENTRE ALUMINIUM ET BOIS COMPOSITE 2 - RÉSISTANCE À LA DÉLAMINATION SELON JIS-K-5600-5-6 3 - RÉSISTANCE À LA DÉLAMINATION FACE À UNE VARIATION EXTRÊME DES TEMPÉRATURES ET DU TAUX D’HUMIDITÉ 4 - TESTS DE DURABILITÉ, DESCRIPTION DES PROCESSUS SELON NORME JIS A1415 5 - VIEILLISSEMENT AUX RAYONS UV SELON NORME JIS-K1571 6 - VIEILLISSEMENT AUX RAYONS UV (TEST PROPRIÉTAIRE) 7 - VARIATIONS DES TEINTES SELON NORME JIS K5400 ET JIS K5600 8 - VARIATIONS DES TEINTES SELON NORME DIN EN ISO 11341 9 - TEST EN MILIEU...

annexe 1 : Résistance à la propagation de l’humidité entre aluminium et bois composite Objet Application d’encre sur la surface du produit au niveau des plans de coupes. Date d’exécution 02.11.2012 Produit Soleo, Careo, Vertigo, Diameo Résultat Après une semaine dans un bain d’encre, aucune trace de pénétration de l’encre entre la couche de bois composite et l’aluminium n’a été constatée. Le produit peut se travailler comme un profilé aluminium sans précaution particulière. annexe 2 : Résistance à la délamination selon JIS-K-5600-5-6 Objet Résistance au détachement de la couche en bois...

annexe 8 : Variations des teintes selon norme din en ISO 11341 annexe 13 : Dureté brinell, résistance à l’abrasion Objet Changement de teinte et d’éclat dû à l’exposition à la météo et aux radiations solaires, selon la norme DIN EN ISO 11341. Objet Mesure de la résistance au poinçonnement (talon aiguille) et mesure de la perte de poids causée par l’usure due à la circulation des piétons. Date d’obtention 02.07.2013 Organisme Institut für Oberflächentechnik GmbH (ifo), Allemagne Produit testé Résultat profilé Soleo a une dureté supérieure au teck Le et la perte de poids due à l’usure est...

annexe 16 : Reaction au feu M2 selon annexe 18 : Recherche des metauxnormes NF P 92-507 et NF P 92-501 lourds selon norme JIS K01022 Objet Essai de reaction au feu par rayonnement Securite contre I’incendie NF P 92-507 (2004) Reaction au feu des materiaux NF P 92-501 (1995) Date d’obtention 9.01.2019 Presence de metaux lourds et emission de formaldehyde. Organisme Produit Resultat LNE (Laboratoire National de metrologie et d'essais) Soleo, Careo, Vertigo, Diameo Obtention du classement M2. Date d’execution Organisme Produit Resultats 20.12.2012 Chemical Evaluation and Research Institute,...

Water Penetration Test Tested product: Soleo Concerned products: Soleo, Careo, Vertigo, Diameo 1. Objective The objective of this test was to examine the strength of the interface between the WPC skin and the Aluminum 6063. By applying ink to the product it can be determined if there is any notable penetration between the Aluminum layer and the WPC core over a period of 1 week. The test samples are treated by accelerated exposure to hot and cold temperatures: 2 hours at -30°C and 2 hours at 80°C for 50 cycles. Dip the WPC-Aluminum Hybrid samples into a tank filled with 40cm of liquid ink...

Resistance to Peeling off of Surface Material Tested product: Soleo Concerned products: Soleo, Careo, Vertigo, Diameo 3. Procedure This testing standard is defined by JIS-K-a5600-5-6 (Testing methods for paints - Part 5: Mechanical property of film - Section 6: Adhesion test). It specifies a test method for assessing the resistance of WPC surface layer to separation from the Aluminum surface when a right angle lattice pattern is cut into the WPC surface layer, penetrating through to the Aluminum surface. The property measured by this empirical test procedure depends among other factors, on...

Peel-off Test under High Temperature, Humidity & Hot Water Tested product: Soleo Concerned products: Soleo, Careo, Vertigo, Diameo Test Method Pictures 1 and 2 show no cracks nor peeled off WPC from the aluminium surface was found. A thinner WPC layer does not decrease the compatibility between the WPC layer and the aluminium surface. The thickness of the WPC layer does not reduce the durability or longevity of the hybrid profile. The aging process of WPC is not related to its thickness. A hybrid profile with a 1mm WPC layer needs to be extruded and sanded with greater care and under...

1. The mechanical property of WPC-Aluminum Hybrid products is investigated using the Japan Industrial Standard (JIS) test methods, methods of analysis and inspection aproach. 2. Since there are variety of testing methods to comply with a variety applications and usage environment the testing method shall be chosen according to client technical needs. 3. We are commited to continuously review and improve testing methods in order to increase product quality. CAHIER TECHNIQUE VERTIGO

Methods Used for Durability Tests Durability Evaluation Results Tested product: Soleo Concerned products: Soleo, Careo, Vertigo, Diameo Test The mechanical property of WPC-Aluminum Hybrid products is investigated using the Japan Industrial Standard (JIS) test methods, methods of analysis and inspection aproach. Immersed in water at room a variety applications and usage environment the testing Since there are variety of testing methods to comply withtemperature Immersion No Peel off method shall be chosen according to client technical needs. Continuously accelerated for 30 days We are...