MULTITOP® ENDURO Metallic‐siliceous hardener for industrial floors – WTW system (wet to wet) CT‐C50‐F10‐A6PRODUKTU PRODUKTU DESCRIPTION MULTITOP® ENDURO WTW is a metallic‐siliceous, surface hardener (WTW ‐ wet to wet) for monolithic concrete floors. It contains hard aggregate, high‐performance cements and proper admixtures and pigments. Applied and troweled on freshly‐made concrete, it creates a coloured, marble‐like, abrasion and dusting resistant, smooth floor of increased resistance to the penetration with oils, grease etc. New surface‐hardened floors of high hardness and resistance to abrasion and dusting in medium traffic facilities – produc‐ tion plants, warehouses, logistic centres as well as in food and pharmaceutical industry facilities etc. High dusting resistance High impact resistance Easy to clean Sealed and non‐dusting surface Frost‐resistant Wide range of colours CONCRETE SLAB BAUTECH WTW SYSTEM floors are used on surfaces of freshly‐made low‐shrinkage concrete:  class C20/25 or higher  w/c ratio ≤ 0,50  amount of cement ≤ 350 kg/m3  alkali contents in cement <0,5%  cement CEM I, CEM II/A‐S, CEM II/B‐S or CEM III/A  aggregate ≤ 16 mm  contents of fraction ≤ 0.25 mm ‐ min. 4%  sand point about 35%  total amount of cement and aggregate of fraction ≤0.25 mm – max. 450 kg/m3  addition of steel fibres BAUMIX and polypropylene fibers BAUCON by recommendation of BAUTECH  consistence on the construction site: S3, Abrams cone slump about 12 cm. Addition of steel fibres decreases the slump. In case of outdoor surfaces, concrete of exposure class XF4 should be used. CAUTION! Do not add any volatile ashes, as these tend to accumulate in the top layer of the slab, which may cause the dusting of the floor or detachments of the hardener. It is forbidden to add water to con‐ crete mixture in order to increase its workability. This causes a signifi‐ cant loss of the strength of the concrete and a clear increase of the chemical and physical shrinkage, leading to the creation of uncon‐ trolled scratches and cracks. The concrete must be properly compacted. APPLICATION CONDITIONS The temperature of the ambient and foundation during the works and for the next 5 days should be between +5°C and +30°C. The surface made should be protected from losing water too quickly as a result of, for example, high temperatures, draught, sunlight operation etc. In order to ensure high quality and uniform colour, all works should be performed with suitable tools in an area protected from dust, EPS balls and similar impurities. To make the floor with “wet on wet” method surface hardener MULTITOP® ENDURO is used. Before the mortar is spread, the concrete must achieve proper hardness. The setting time of con‐ crete depends on the temperature, relative humidity of the air etc. The surface of the concrete must not get too hard, therefore its condition must be frequently checked. As a result, selection of the optimal moment to begin application of the mortar will be possible. The works may be commenced when the imprints of feet on the concrete are not deeper than 3‐4 mm. Remove excess of cement grout from the surface and refresh it with a disc. Then begin the spreading of prepared MULTITOP® ENDURO mortar. Preparation of the mortar: To 3.0‐3.5 l of clean, cold water pour 30 kg (a bag) of dry mixture and mix for 3‐4 minutes in a concrete mixer or with a slow‐ running drill with a mixer until a homogenous mass is obtained. Spill the prepared mortar on the foundation and spread to the desired thickness using a distance scraper or float along with a laser levelling instrument or spacer strip, while smoothing the surface with a long float until uniform, smooth structure is ob‐ tained. Prepare portions which will be used within about 15 min. Do not add more water than the instructions indicate, as this will de‐ crease the strength and increase the contraction of the mortar. In the wintertime the material should be kept in a heated room prior to mixing. Low temperature of the material may cause that some additions will not be able to dissolve during mixing. Too high temperature of the material will decrease the spread of the mor‐ tar and result in too quick bonding. Perform the subsequent stages of troweling with blades set gradually at increasing angles. CURING Immediately after the troweling is completed, the whole surface should be treated with a selected preparation in order to prevent too quick loss of water: BAUSEAL® EKO A water‐diluted sealer for industrial floors applied with the spraying method, with a low‐pressure sprayer. Sealer should be applied once, with a thin layer, paying attention that no puddles are left. Efficiency: 1 litre per 8‐12 m2 BAUSEAL® ENDURO A solv

NANOSEAL® Lithium and polymer based agent for the maintenance, strengthening and sealing of concrete surfaces. Thanks to the penetration and hard‐ ening of concrete in molecular structure, it allows to obtain a highly resistant cement matrix of extreme physical and chemical properties. Additional modification with a specially selected polymer binding agent provides the maximum level of sealing the concrete by bonding those ingredients of the concrete matrix that are devoid of free cal‐ cium compounds. NANOSEAL should be applied evenly on the surface with the spraying ...