ALPIlignum Technical Features ⁄ ALPIlignum ⁄ ALPIlignum is a decorative multilaminar wood veneer that complies with standard ISO 18775. Average Weight Composition ⁄ Poplar wood and/or Ayous wood, and/or Basswood Moisture content Being a wood product, ALPIlignum’s moisture content may vary depending on environmental conditions during transport and storage. Ayous Veneer Poplar Veneer Basswood Veneer Veneer dimension may be customized upon request and for specific product lines. *With the exception of some product lines. with the following nominal thickness intervals We can customize veneer...

Open the catalog to page 3

ALPIlignum Technical Features ⁄ Formaldehyde Emission ⁄ In compliance with E1 (analyzed according to EN 717). On request ALPI can supply ALPIlignum with two levels of formaldehyde emissions below the E1 standard: BE - ALPIlignum with a formaldehyde emission level equal to a fraction of the E1 standard. ZeroF - ALPIlignum without added formaldehyde. It is in any event impossible to guarantee a complete absence of formaldehyde in ALPIlignum wood veneers as formaldehyde is a naturally-occurring substance in wood. Light Fastness ⁄ ALPIlignum is not a finished product and, therefore its...

Open the catalog to page 4

Veneering ⁄ Glueing With Urea Glues ALPIlignum veneer can be glued on all wood backing using by means of urea glues. Different kinds of backing must be tested and assessed on a case-by-case basis. The quantity of glue to be used per square meter depends on the base type and thickness, on the veneer structure (quartered cut, tangential cut, burl, etc.), on its thickness and on the type of pressing. It is generally advisable not to use more than 150 g/m² of glue at pressures ranging from 1.5 to 5 bars. The recommended veneering temperature may range between 85°C and 120°C. The glue may be...

Open the catalog to page 5

ALPIkord Technical Features ⁄ Light Gloss-Bright Gloss ⁄ Nominal Thickness Postforming Temperature Halo caused by acetone Bending Radius* Dimensional Variations En 438-2, 17 (2005) Abrasion Resistance* En 438-2, 10 (2005) Stain Resistance En 438-2, 26 (2005) Lightfastness (Xenotest) En 438-2, 27 (2005) Formaldehyde Emission En 717-2 ALPIlignum Wood Veneer Lacquer Finish Phenolic Backing

Open the catalog to page 6

ALPIrobur Technical Features ⁄ Soft-Matt-Pore-Brushed ⁄ Fireproof IMO MED Certificate ⁄ Nominal Thickness Dimensional Variations ALPIlignum Wood Veneer High Resistance Finish Phenolic Backing

Open the catalog to page 7

ALPIkord - ALPIrobur Recommendations for Use ⁄ Application Tips ⁄ To ensure appropriate counterbalancing it is advisable to use the same type of product, although the process may also be conducted using HPL matching the characteristics of the face. In any case, specific production tests should be carried out to evaluate the suitability of the product utilized over time (48/72 hours). Application with Steel Plate Press ⁄ The utmost attention is required when using a steel plate press. It is necessary a perfect cleaning of the plates to avoid dents or damage to the finished surface. Damages...